S-Plastics Verton MT00E resin is a compound based on Polypropylene resin containing Proprietary Thermal Filler. Added features of this
material include: Thermally Conductive.
Property
| TYPICAL PROPERTIES (1) | | | |
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, break | 22 | MPa | ASTM D 638 |
| Tensile Strain, break | 1 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 90750 | MPa | ASTM D 638 |
| Flexural Stress | 44 | MPa | ASTM D 790 |
| Tensile Stress, break | 22 | MPa | ISO 527 |
| Tensile Strain, break | 0.9 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 8650 | MPa | ISO 527 |
| Flexural Stress | 44 | MPa | ISO 178 |
| Flexural Modulus | 8160 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched, 23°C | 74 | J/m | ASTM D 4812 |
| Izod Impact, notched, 23°C | 10 | J/m | ASTM D 256 |
| Izod Impact, unnotched 80*10*4 +23°C | 7 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 4 | kJ/m² | ISO 180/1A |
| THERMAL | Value | Unit | Standard |
| Thermal Conductivity | 1.1 | W/m-°C | ASTM E 1530 |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 137 | °C | ISO 75/Bf |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 103 | °C | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Density | 1.952 | g/cm³ | ASTM D 792 |
| Mold Shrinkage, flow, 24 hrs | 0.9 | % | ASTM D 955 |
| Mold Shrinkage, xflow, 24 hrs | 0.7 | % | ASTM D 955 |
| Mold Shrinkage, flow, 24 hrs | 0.95 | % | ISO 294 |
| Mold Shrinkage, xflow, 24 hrs | 0.74 | % | ISO 294 |
| Wear Factor Washer | 1131 | 10^-10 in^5-min/ft-lb-hr | ASTM D 3702 Modified |
| Dynamic COF | 0.43 | - | ASTM D 3702 Modified |
| Static COF | 0.48 | - | ASTM D 3702 Modified |
| Density | 1.94 | g/cm³ | ISO 1183 |
| Source GMD, last updated:10/04/2004 | | |
Processing
| Parameter | | |
| Injection Molding | Value | Unit |
| Drying Temperature | 80 | °C |
| Drying Time | 4 | hrs |
| Melt Temperature | 210 - 225 | °C |
| Front - Zone 3 Temperature | 215 - 225 | °C |
| Middle - Zone 2 Temperature | 205 - 215 | °C |
| Rear - Zone 1 Temperature | 195 - 205 | °C |
| Mold Temperature | 25 - 50 | °C |
| Back Pressure | 0.2 - 0.3 | MPa |
| Screw Speed | 30 - 60 | rpm |
| Source GMD, last updated:10/04/2004 | |