| TYPICAL PROPERTIES (1) | | | |
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, brk, Type I, 5 mm/min | 50 | MPa | ASTM D 638 |
| Tensile Strain, brk, Type I, 5 mm/min | 0.7 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 10230 | MPa | ASTM D 638 |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 71 | MPa | ASTM D 790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 8820 | MPa | ASTM D 790 |
| Tensile Stress, break, 5 mm/min | 44 | MPa | ISO 527 |
| Tensile Strain, break, 5 mm/min | 0.6 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 8910 | MPa | ISO 527 |
| Flexural Stress | 68 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 8760 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched, 23°C | 130 | J/m | ASTM D 4812 |
| Izod Impact, notched, 23°C | 23 | J/m | ASTM D 256 |
| Multiaxial Impact | 2 | J | ISO 6603 |
| Instrumented Impact Total Energy, 23°C | 8 | J | ASTM D 3763 |
| Izod Impact, unnotched 80*10*4 +23°C | 8 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 2 | kJ/m² | ISO 180/1A |
| THERMAL | Value | Unit | Standard |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 97 | °C | ASTM D 648 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 92 | °C | ASTM D 648 |
| CTE, -30°C to 30°C, flow | 5.26E+01 | 1/°C | ASTM D 696 |
| CTE, -30°C to 30°C, xflow | 5.33E+01 | 1/°C | ASTM D 696 |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 97 | °C | ISO 75/Bf |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 92 | °C | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Specific Gravity | 1.31 | - | ASTM D 792 |
| Density | 1.3 | g/cm³ | ASTM D 792 |
| Moisture Absorption, 50% RH, 24 hrs | 0.05 | % | ASTM D 570 |
| Mold Shrinkage, flow, 24 hrs (5) | 0.1 - 0.4 | % | ASTM D 955 |
| Mold Shrinkage, xflow, 24 hrs (5) | 0.3 - 0.6 | % | ASTM D 955 |
| Moisture Absorption (23°C / 50% RH) | 0.06 | % | ISO 62 |
| Source GMD, last updated:2009/07/28 | | |