| MECHANICAL | Value | Unit | Standard | |
| Tensile Stress, break | 83 | MPa | ASTM D 638 | |
| Tensile Strain, break | 3.8 | % | ASTM D 638 | |
| Tensile Modulus, 50 mm/min | 4170 | MPa | ASTM D 638 | |
| Flexural Stress | 144 | MPa | ASTM D 790 | |
| Flexural Modulus | 4280 | MPa | ASTM D 790 | |
| Tensile Stress, break | 84 | MPa | ISO 527 | |
| Tensile Strain, break | 3.6 | % | ISO 527 | |
| Tensile Modulus, 1 mm/min | 4100 | MPa | ISO 527 | |
| Flexural Stress | 117 | MPa | ISO 178 | |
| Flexural Modulus | 3920 | MPa | ISO 178 | |
| IMPACT | Value | Unit | Standard | |
| Izod Impact, unnotched, 23°C | 907 | J/m | ASTM D 4812 | |
| Izod Impact, notched, 23°C | 96 | J/m | ASTM D 256 | |
| Instrumented Impact Energy @ peak, 23°C | 13 | J | ASTM D 3763 | |
| Multiaxial Impact | 9 | J | ISO 6603 | |
| Izod Impact, unnotched 80*10*4 +23°C | 61 | kJ/m² | ISO 180/1U | |
| Izod Impact, notched 80*10*4 +23°C | 8 | kJ/m² | ISO 180/1A | |
| THERMAL | Value | Unit | Standard | |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 141 | °C | ASTM D 648 | |
| HDT, 1.82 MPa, 3.2mm, unannealed | 136 | °C | ASTM D 648 | |
| CTE, -40°C to 40°C, flow | 3.78E-05 | 1/°C | ASTM E 831 | |
| CTE, -40°C to 40°C, xflow | 5.4E-05 | 1/°C | ASTM E 831 | |
| CTE, -40°C to 40°C, flow | 3.82E-05 | 1/°C | ISO 11359-2 | |
| CTE, -40°C to 40°C, xflow | 5.35E-05 | 1/°C | ISO 11359-2 | |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 141 | °C | ISO 75/Bf | |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 137 | °C | ISO 75/Af | |
| PHYSICAL | Value | Unit | Standard | |
| Density | 1.28 | g/cm³ | ASTM D 792 | |
| Moisture Absorption, 50% RH, 24 hrs | 0.1 | % | ASTM D 570 | |
| Mold Shrinkage, flow, 24 hrs | 0.4 | % | ASTM D 955 | |
| Mold Shrinkage, xflow, 24 hrs | 0.5 | % | ASTM D 955 | |
| Mold Shrinkage, flow, 24 hrs | 0.43 | % | ISO 294 | |
| Mold Shrinkage, xflow, 24 hrs | 0.51 | % | ISO 294 | |
| Density | 1.27 | g/cm³ | ISO 1183 | |
| FLAME CHARACTERISTICS | Value | Unit | Standard | |
| UL Compliant, 94V-1 Flame Class Rating (3)(4) | 3 | mm | UL 94 by GE | |
| Source GMD, last updated:06/13/2007 | | | | |