S-Plastics Thermocomp UF007AS resin is a compound based on Polyphthalamide resin containing Glass Fiber. Added features include HeatStabilized .
Property
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, break, 5 mm/min | 194 | MPa | ISO 527 |
| Tensile Strain, break, 5 mm/min | 2 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 12100 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 279 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 9600 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched 80*10*4 +23°C | 45 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 11 | kJ/m² | ISO 180/1A |
| THERMAL | Value | Unit | Standard |
| CTE, 23°C to 60°C, flow | 2.2E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C to 60°C, xflow | 5.9E-05 | 1/°C | ISO 11359-2 |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 269 | °C | ISO 75/Af |
| Relative Temp Index, Elec | 130 | °C | UL 746B |
| Relative Temp Index, Mech w/impact | 65 | °C | UL 746B |
| Relative Temp Index, Mech w/o impact | 115 | °C | UL 746B |
| PHYSICAL | Value | Unit | Standard |
| Mold Shrinkage, flow | 0.15 | % | S-Plastics Method |
| Density | 1.46 | g/cm³ | ISO 1183 |
| FLAME CHARACTERISTICS | Value | Unit | Standard |
| UL Recognized, 94HB Flame Class Rating (3) | 0.75 | mm | UL 94 |
| Source GMD, last updated:11/27/2007 | | |
Processing
| Parameter | | |
| Injection Molding | Value | Unit |
| Drying Temperature | 120 - 150 | °C |
| Drying Time | 4 | hrs |
| Maximum Moisture Content | 0.15 - 0.15 | % |
| Melt Temperature | 315 - 330 | °C |
| Front - Zone 3 Temperature | 325 - 340 | °C |
| Middle - Zone 2 Temperature | 315 - 325 | °C |
| Rear - Zone 1 Temperature | 310 - 320 | °C |
| Mold Temperature | 140 - 165 | °C |
| Back Pressure | 0.2 - 0.3 | MPa |
| Screw Speed | 30 - 60 | rpm |
| Source GMD, last updated:11/27/2007 | |