S-Plastics Thermocomp MFB429 resin is a compound based on Polypropylene resin containing Flame Retardant. Added features of this material
include: Chemically Coupled, Flame Retardant.
Property
| TYPICAL PROPERTIES (1) | | | |
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, break | 41 | MPa | ASTM D 638 |
| Tensile Strain, break | 2.6 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 5580 | MPa | ASTM D 638 |
| Flexural Stress | 68 | MPa | ASTM D 790 |
| Flexural Modulus | 4130 | MPa | ASTM D 790 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched, 23°C | 267 | J/m | ASTM D 4812 |
| Izod Impact, notched, 23°C | 42 | J/m | ASTM D 256 |
| THERMAL | Value | Unit | Standard |
| HDT, 1.82 MPa, 3.2mm, unannealed | 130 | °C | ASTM D 648 |
| PHYSICAL | Value | Unit | Standard |
| Density | 1.48 | g/cm³ | ASTM D 792 |
| Source GMD, last updated:12/06/2005 | | |
Processing
| THESE PROPERTY VALUES ARE NOT INTENDED FOR SPECIFICATION PURPOSES. | | |
| PLEASE CHECK WITH YOUR (LOCAL SALES OFFICE) FOR AVAILABILITY IN YOUR REGION | | |
(1) Typical values only. Variations within normal tolerances are possible for various colors. All values are measured after at least 48 hours
storage at 23°C/50% relative humidity. All properties, except the melt volume and melt flow rates, are measured on injection molded
samples. All samples tested under ISO test standards are prepared according to ISO 294. |
| (2) Only typical data for selection purposes. Not to be used for part or tool design. | | | |
| (3) This rating is not intended to reflect hazards presented by this or any other material under actual fire conditions. | |
| (4) Internal measurements according to UL standards. | | | |