| TYPICAL PROPERTIES (1) | | | |
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yld, Type I, 5 mm/min | 0 | MPa | ASTM D 638 |
| Tensile Stress, brk, Type I, 5 mm/min | 183 | MPa | ASTM D 638 |
| Tensile Strain, yld, Type I, 5 mm/min | 0 | % | ASTM D 638 |
| Tensile Strain, brk, Type I, 5 mm/min | 2.2 | % | ASTM D 638 |
| Tensile Modulus, 5 mm/min | 9990 | MPa | ASTM D 638 |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 170 | MPa | ASTM D 790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 9300 | MPa | ASTM D 790 |
| Tensile Stress, yield, 5 mm/min | 0 | MPa | ISO 527 |
| Tensile Stress, break, 5 mm/min | 120 | MPa | ISO 527 |
| Tensile Strain, yield, 5 mm/min | 0 | % | ISO 527 |
| Tensile Strain, break, 5 mm/min | 1.9 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 1030 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 155 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 7900 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, notched, 23°C | 45 | J/m | ASTM D 256 |
| Izod Impact, notched 80*10*4 +23°C | 5 | kJ/m² | ISO 180/1A |
| THERMAL | Value | Unit | Standard |
| HDT, 1.82 MPa, 3.2mm, unannealed | 173 | °C | ASTM D 648 |
| Vicat Softening Temp, Rate B/120 | 0 | °C | ISO 306 |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 176 | °C | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Specific Gravity | 1.33 | - | ASTM D 792 |
| Melt Flow Rate, 315°C/5.0 kgf | 7.7 | g/10 min | ASTM D 1238 |
| Density | 1.33 | g/cm³ | ISO 1183 |
| Melt Volume Rate, MVR at 320°C/2.16 kg | 2 | cm³/10 min | ISO 1133 |
| Source GMD, last updated:11/01/2006 | | |