S-Plastics Stat-kon DE004 resin is a compound based on Polycarbonate resin containing Carbon Fiber. Added features of this material include:
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, break | 120 | MPa | ASTM D 638 |
| Tensile Strain, break | 2.2 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 10890 | MPa | ASTM D 638 |
| Flexural Stress | 196 | MPa | ASTM D 790 |
| Flexural Modulus | 9790 | MPa | ASTM D 790 |
| Tensile Stress, break | 114 | MPa | ISO 527 |
| Tensile Strain, break | 1.6 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 10600 | MPa | ISO 527 |
| Flexural Stress | 188 | MPa | ISO 178 |
| Flexural Modulus | 9780 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched, 23°C | 490 | J/m | ASTM D 4812 |
| Izod Impact, notched, 23°C | 73 | J/m | ASTM D 256 |
| Instrumented Impact Energy @ peak, 23°C | 15 | J | ASTM D 3763 |
| Multiaxial Impact | 3 | J | ISO 6603 |
| Izod Impact, unnotched 80*10*4 +23°C | 33 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 6 | kJ/m² | ISO 180/1A |
| THERMAL | Value | Unit | Standard |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 147 | °C | ASTM D 648 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 144 | °C | ASTM D 648 |
| CTE, -40°C to 40°C, flow | 1.4E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C to 40°C, xflow | 4.24E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C to 40°C, flow | 1.33E-05 | 1/°C | ISO 11359-2 |
| CTE, -40°C to 40°C, xflow | 4.25E-05 | 1/°C | ISO 11359-2 |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 149 | °C | ISO 75/Bf |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 144 | °C | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Density | 1.27 | g/cm³ | ASTM D 792 |
| Moisture Absorption, 50% RH, 24 hrs | 0.15 | % | ASTM D 570 |
| Mold Shrinkage, flow, 24 hrs | 0.04 - 0.1 | % | ASTM D 955 |
| Mold Shrinkage, xflow, 24 hrs | 0.3 - 0.4 | % | ASTM D 955 |
| Mold Shrinkage, flow, 24 hrs | 0.04 - 0.09 | % | ISO 294 |
| Mold Shrinkage, xflow, 24 hrs | 0.37 - 0.45 | % | ISO 294 |
| Density | 1.27 | g/cm³ | ISO 1183 |
| Moisture Absorption (23°C / 50% RH) | 0.21 | % | ISO 62 |
| ELECTRICAL | Value | Unit | Standard |
| Surface Resistivity | 1.E+01 - 1.E+04 | Ohm | ASTM D 257 |
| Source GMD, last updated:09/30/2004 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 120 | °C |
| Drying Time | 4 | hrs |
| Maximum Moisture Content | 0.02 | % |
| Melt Temperature | 305 - 325 | °C |
| Front - Zone 3 Temperature | 320 - 330 | °C |
| Middle - Zone 2 Temperature | 310 - 320 | °C |
| Rear - Zone 1 Temperature | 295 - 305 | °C |
| Mold Temperature | 80 - 110 | °C |
| Back Pressure | 0.2 - 0.3 | MPa |
| Screw Speed | 30 - 60 | rpm |
| Source GMD, last updated:09/30/2004 | ||
Other related products we recommend:
| For more information please download the datesheet | |
 | S-Plastics Stat-kon DE004.pdf |