S-Plastics Colorcomp JX91550 resin is a compound based on Polyethersulfone resin containing Unfilled Custom Color.
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yield | 77 | MPa | ASTM D 638 |
| Tensile Stress, break | 58 | MPa | ASTM D 638 |
| Tensile Strain, yield | 5.6 | % | ASTM D 638 |
| Tensile Strain, break | 13.5 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 2930 | MPa | ASTM D 638 |
| Flexural Stress | 122 | MPa | ASTM D 790 |
| Flexural Modulus | 2890 | MPa | ASTM D 790 |
| Tensile Stress, yield | 78 | MPa | ISO 527 |
| Tensile Stress, break | 53 | MPa | ISO 527 |
| Tensile Strain, yield | 6.2 | % | ISO 527 |
| Tensile Strain, break | 23.4 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 2830 | MPa | ISO 527 |
| Flexural Stress | 118 | MPa | ISO 178 |
| Flexural Modulus | 2920 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched, 23°C | NB | J/m | ASTM D 4812 |
| Izod Impact, notched, 23°C | 53 | J/m | ASTM D 256 |
| Instrumented Impact Energy @ peak, 23°C | 19 | J | ASTM D 3763 |
| Multiaxial Impact | 32 | J | ISO 6603 |
| Izod Impact, unnotched 80*10*4 +23°C | NB | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 4 | kJ/m² | ISO 180/1A |
| THERMAL | Value | Unit | Standard |
| HDT, 1.82 MPa, 3.2mm, unannealed | 176 | °C | ASTM D 648 |
| CTE, -40°C to 40°C, flow | 5.05E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C to 40°C, xflow | 5.14E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C to 40°C, flow | 5.07E-05 | 1/°C | ISO 11359-2 |
| CTE, -40°C to 40°C, xflow | 5.15E-05 | 1/°C | ISO 11359-2 |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 187 | °C | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Density | 1.49 | g/cm³ | ASTM D 792 |
| Mold Shrinkage, flow, 24 hrs | 0.6 - 0.8 | % | ASTM D 955 |
| Mold Shrinkage, xflow, 24 hrs | 0.7 - 0.9 | % | ASTM D 955 |
| Mold Shrinkage, flow, 24 hrs | 0.6 - 0.8 | % | ISO 294 |
| Mold Shrinkage, xflow, 24 hrs | 0.7 - 0.9 | % | ISO 294 |
| Density | 1.49 | g/cm³ | ISO 1183 |
| Moisture Absorption (23°C / 50% RH) | 0.76 | % | ISO 62 |
| Source GMD, last updated:10/05/2004 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 120 - 150 | °C |
| Drying Time | 4 | hrs |
| Maximum Moisture Content | 0.05 | % |
| Melt Temperature | 355 - 370 | °C |
| Front - Zone 3 Temperature | 370 - 380 | °C |
| Middle - Zone 2 Temperature | 360 - 370 | °C |
| Rear - Zone 1 Temperature | 345 - 355 | °C |
| Mold Temperature | 140 - 150 | °C |
| Back Pressure | 0.3 - 0.7 | MPa |
| Screw Speed | 60 - 100 | rpm |
| Source GMD, last updated:10/05/2004 | ||
| For more information please download the datesheet | |
 | S-Plastics Colorcomp JX91550.pdf |