S-Plastics Colorcomp R1000S resin is a compound based on Nylon 66 resin containing Unfilled Glow In the Dark Custom Color. Added features
of this material include: Heat Stabilized.
Property
| TYPICAL PROPERTIES (1) | | | |
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yield | 75 | MPa | ISO 527 |
| Tensile Strain, yield | 10 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 3400 | MPa | ISO 527 |
| Flexural Stress | 11 | MPa | ISO 178 |
| Flexural Modulus | 3200 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, notched 80*10*4 +23°C | 4 | kJ/m² | ISO 180/1A |
| THERMAL | Value | Unit | Standard |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 75 | °C | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Density | 1.22 | g/cm³ | ASTM D 792 |
| Density | 1.23 | g/cm³ | ISO 1183 |
| Source GMD, last updated:09/28/2004 | | |
Processing
| Parameter | | |
| Injection Molding | Value | Unit |
| Drying Temperature | 80 | °C |
| Drying Time | 4 | hrs |
| Maximum Moisture Content | 0.15 - 0.25 | % |
| Melt Temperature | 265 - 275 | °C |
| Front - Zone 3 Temperature | 260 - 270 | °C |
| Middle - Zone 2 Temperature | 255 - 265 | °C |
| Rear - Zone 1 Temperature | 250 - 260 | °C |
| Mold Temperature | 60 - 100 | °C |
| Back Pressure | 0.2 - 0.3 | MPa |
| Screw Speed | 30 - 60 | rpm |
| Source GMD, last updated:09/28/2004 | |