S-Plastics Geloy CR7020 resin is ASA copolymer. Profile/sheet coextrusion over ABS. Excellent weatherability, good flow/aesthetics and high impact.
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yld, Type I, 50 mm/min | 41 | MPa | ASTM D 638 |
| Tensile Stress, brk, Type I, 50 mm/min | 34 | MPa | ASTM D 638 |
| Tensile Strain, brk, Type I, 50 mm/min | 40 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 1790 | MPa | ASTM D 638 |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 58 | MPa | ASTM D 790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 1790 | MPa | ASTM D 790 |
| Hardness, Rockwell R | 86 | - | ASTM D 785 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, notched, 23°C | 320 | J/m | ASTM D 256 |
| Izod Impact, notched, -30°C | 58 | J/m | ASTM D 256 |
| Gardner Impact (Procedure B) | 10675 | J/m | ASTM D 4226 |
| Instrumented Impact Total Energy, 23°C | 25 | J | ASTM D 3763 |
| THERMAL | Value | Unit | Standard |
| Vicat Softening Temp, Rate B/50 | 99 | °C | ASTM D 1525 |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 87 | °C | ASTM D 648 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 76 | °C | ASTM D 648 |
| HDT, 1.82 MPa, annealed | 95 | °C | ASTM D 648 |
| HDT, 0.45 MPa, 6.4 mm, unannealed | 90 | °C | ASTM D 648 |
| HDT, 1.82 MPa, 6.4 mm, unannealed | 79 | °C | ASTM D 648 |
| CTE, -40°C to 40°C, flow | 8.64E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C to 40°C, xflow | 9.18E-05 | 1/°C | ASTM E 831 |
| CTE, -30°C to 0°C, flow | 8.46E-05 | 1/°C | ASTM E 831 |
| CTE, 0°C to 100°C, flow | 9.E-05 | 1/°C | ASTM E 831 |
| Relative Temp Index, Elec | 50 | °C | UL 746B |
| Relative Temp Index, Mech w/impact | 50 | °C | UL 746B |
| Relative Temp Index, Mech w/o impact | 50 | °C | UL 746B |
| PHYSICAL | Value | Unit | Standard |
| Specific Gravity | 1.06 | - | ASTM D 792 |
| Water Absorption, equilibrium, 23C | 0.55 | % | ASTM D 570 |
| Mold Shrinkage, flow, 3.2 mm | 0.5 - 0.7 | % | S-Plastics Method |
| Melt Flow Rate, 220°C/10.0 kgf | 7 | g/10 min | ASTM D 1238 |
| Melt Flow Rate, 260°C/5.0 kgf | 13 | g/10 min | ASTM D 1238 |
| OPTICAL | Value | Unit | Standard |
| Gloss, untextured, 60 degrees | 95 | - | ASTM D 523 |
| ELECTRICAL | Value | Unit | Standard |
| Surface Resistivity | >1.E+15 | Ohm | ASTM D 257 |
| Dielectric Strength, in oil, 3.2 mm | 15.9 | kV/mm | ASTM D 149 |
| Relative Permittivity, 50/60 Hz | 5.2 | - | ASTM D 150 |
| Relative Permittivity, 1 MHz | 3.21 | - | ASTM D 150 |
| Dissipation Factor, 50/60 Hz | 0.15 | - | ASTM D 150 |
| Dissipation Factor, 1 MHz | 0.026 | - | ASTM D 150 |
| Hot Wire Ignition {PLC) | 3 | PLC Code | UL 746A |
| High Ampere Arc Ign, surface {PLC} | 0 | PLC Code | UL 746A |
| Comparative Tracking Index (UL) {PLC} | 0 | PLC Code | UL 746A |
| FLAME CHARACTERISTICS | Value | Unit | Standard |
| UL Recognized, 94HB Flame Class Rating (3) | 1.49 | mm | UL 94 |
| UV-light, water exposure/immersion | F2 | - | UL 746C |
| Source GMD, last updated:03/29/1999 | |||
| Parameter | ||
| Profile Extrusion | Value | Unit |
| Drying Temperature | 80 - 90 | °C |
| Drying Time | 3 - 6 | hrs |
| Drying Time (Cumulative) | 12 | hrs |
| Minimum Moisture Content | 0.02 | % |
| Melt Temperature | 225 - 255 | °C |
| Barrel - Zone 1 Temperature | 205 - 215 | °C |
| Barrel - Zone 2 Temperature | 215 - 230 | °C |
| Barrel - Zone 3 Temperature | 220 - 240 | °C |
| Barrel - Zone 4 Temperature | 225 - 245 | °C |
| Adapter Temperature | 225 - 245 | °C |
| Die Temperature | 225 - 245 | °C |
| Calibrator Temperature | 15 - 65 | °C |
| Source GMD, last updated:03/29/1999 | ||
Other related products we recommend:
| For more information please download the datasheet | |
 | S-Plastics Geloy CR7020.pdf |